The following mainly analyzes the lead-acid battery short circuit caused by excessive charging current, charging voltage of a single battery exceeds 2.4V, internal short-circuit or partial discharge, excessive temperature rise and valve control failure, and summarizes the treatment methods of lead acid battery short circuit as follows:
The construction of a lead acid battery cell is as shown in Fig. 1. It consists of the following parts : Anode or positive terminal (or plate). Cathode or negative terminal (or plate). Electrolyte. Separators. Anode or positive terminal (or plate): The positive plates are also called as anode. The material used for it is lead peroxide (PbO 2).
Construction, Working, Connection Diagram, Charging & Chemical Reaction Figure 1: Lead Acid Battery. The battery cells in which the chemical action taking place is reversible are known as the lead acid battery cells. So it is possible to recharge a lead acid battery cell if it is in the discharged state.
In this article we will discuss about the working of lead-acid battery with the help of diagram. When the sulphuric acid is dissolved, its molecules break up into hydrogen positive ions (2H +) and sulphate negative ions (SO 4– –) and move freely.
Effective repair of the battery can maximize the utilization of the battery and reduce the waste of resources. At the same time, when using lead-acid batteries, we should master the correct use methods and skills to avoid failure caused by misoperation.
Nevertheless, positive grid corrosion is probably still the most frequent, general cause of lead–acid battery failure, especially in prominent applications, such as for instance in automotive (SLI) batteries and in stand-by batteries. Pictures, as shown in Fig. 1 taken during post-mortem inspection, are familiar to every battery technician.